點擊圖片查看大圖東莞旺特公司低價供應(yīng)無鹵阻燃增強PC 500ECR 無溴無氯 聚碳酸酯塑料
沙伯基礎(chǔ)創(chuàng)新PC LEXAN 500ECR 產(chǎn)品特性：含10%玻璃纖維增強，無溴無氯，防火阻燃（2.3mm），良好的剛度
PC 500ECR 物性表：
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Molding Shrinkage - Across Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.31 | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 2 | 2460 | MPa | ASTM D638 |
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength 3 (Yield) | 57 | MPa | ASTM D638 |
| Tensile Stress (Yield) | 60 | MPa | ISO 527-2/5 |
| Tensile Strength 3 (Break) | 48 | MPa | ASTM D638 |
| Tensile Stress (Break) | 45 | MPa | ISO 527-2/5 |
| Tensile Elongation 3 (Yield) | 4.7 | % | ASTM D638 |
| Tensile Strain (Yield) | 5 | % | ISO 527-2/5 |
| Tensile Elongation 3 (Break) | 46 | % | ASTM D638 |
| Tensile Strain (Break) | 7 | % | ISO 527-2/5 |
| Flexural Modulus 4 (50.0 mm Span) | 3120 | MPa | ASTM D790 |
| Flexural Modulus 5 | 3400 | MPa | ISO 178 |
| Flexural Strength 5, 6 | 95 | MPa | ISO 178 |
| Flexural Strength 4 (Break, 50.0 mm Span) | 94 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 11 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength | |||
| -30°C 7 | 9 | kJ/m² | ISO 179/1eA |
| 23°C 7 | 10 | kJ/m² | ISO 179/1eA |
| 23°C 8 | 9 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C 8 | No Break | ||
| -30°C 7 | No Break | ||
| 23°C 7 | No Break | ||
| 23°C 8 | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 100 | J/m | |
| 23°C | 130 | J/m | |
| Notched Izod Impact Strength 9 | ISO 180/1A | ||
| -30°C | 8 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Unnotched Izod Impact (23°C, 6.40 mm) | No Break | ASTM D4812 | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C 10 | No Break | ||
| -30°C 9 | 130 | kJ/m² | |
| 23°C 9 | No Break | ||
| 23°C 10 | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 61 | J | ASTM D3763 |
| Hardness | Nominal Value | Unit | Test Method |
| Ball Indentation Hardness (H 358/30) | 115 | MPa | ISO 2039-1 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 143 | °C | ASTM D648 |
| Heat Deflection Temperature 11 (0.45 MPa, Unannealed, 100 mm Span) | 144 | °C | ISO 75-2/Be |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 136 | °C | ASTM D648 |
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed, 100 mm Span 11 | 136 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 136 | °C | ISO 75-2/Af |
| Heat Deflection Temperature 13 (1.8 MPa, Annealed) | 142 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 14 |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ISO 306/B50 |
| -- | 143 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-40 to 40°C) | 0.000047 | cm/cm/°C | ASTM E831 |
| CLTE - Flow (23 to 80°C) | 0.00004 | cm/cm/°C | ISO 11359-2 |
| CLTE - Transverse (-40 to 40°C) | 0.000085 | cm/cm/°C | ASTM E831 |
| CLTE - Transverse (-40 to 40°C) | 0.000085 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity | > 1.0E+15 | ohm | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohm·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.9 | ||
| 60 Hz | 2.9 | ||
| 1 MHz | 2.8 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.001 | ||
| 60 Hz | 0.001 | ||
| 1 MHz | 0.01 | ||
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 33 | kV/mm | |
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Oil | 16 | kV/mm | |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating - UL | UL 94 | ||
| 2.30 mm | V-0 | ||
| 1.80 mm | V-1 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 36 | % | ISO 4589-2 |
| UL | Nominal Value | Unit | Test Method |
| RTI Str | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Elec | 130 | °C | UL 746 |
| Comparative Tracking Index (CTI) (PLC) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) (PLC) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) (PLC) | PLC 4 | UL 746 | |
| Outdoor Suitability | f2 | UL 746C | |